Nylatron ® GS FILLED NYLON
|
Nylatron ®
NS FILLED NYLON
|
Nylatron ®
GSM NYLON
|
Nylatron ®
GSM-BLUE NYLON
|
Nylatron ®
NSM NYLON
|
MC 901 BLUE NYLON
|
MC 904 BLUE NYLON
|
MC 907 NATURAL
NYLON
|
|
|
|
|
Units
|
ASTM Test Method
|
MoS2 FILLED TYPE 6/6 POLYAMIDE
|
LUBRICATED TYPE 6/6 POLYAMIDE
|
MoS2 FILLED TYPE 6 POLYAMIDE
|
LUBRICATED TYPE 6 POLYAMIDE
|
LUBRICATED TYPE 6 POLYAMIDE
|
MONOCAST HEAT STABILIZED TYPE 6 POLYAMIDE
|
PLASTICIZED HEAT STABILIZED TYPE 6 POLYAMIDE
|
MONOCAST FDA TYPE 6 POLYAMIDE
|
|
MECHANICAL
|
1
|
Strength to
Weight Ratio
|
ksi
|
-
|
|
|
|
|
|
|
|
|
|
2
|
Specific Gravity
@73 F
|
-
|
D792
|
1.16
|
1.18
|
1.16
|
1.15
|
1.15
|
1.15
|
1.15
|
1.15
|
|
3
|
Tensile Strength
@73 F, (ult)/(yld)
|
psi
|
D638
|
12500 (ult)
|
10500(ult)
|
10500(ult)
|
10000(ult)
|
11000(ult)
|
11000(ult)
|
9500(ult)
|
12000(ult)
|
|
4
|
Tensile Modulus
of Elasticity @ 73 F
|
psi
|
D638
|
480000
|
410000
|
400000
|
500000
|
410000
|
400000
|
275000
|
400000
|
|
5
|
Tensile Elongation
at Break @ 73 F
|
%
|
D638
|
25
|
10
|
30
|
35
|
20
|
20
|
50
|
20
|
|
6
|
Flexural Strength
@ 73 F
|
psi
|
D790
|
17000
|
14000
|
16000
|
15000
|
16000
|
16000
|
-
|
16000
|
|
7
|
Flexural Modulus
of Elasticity @ 73 F
|
psi
|
D790
|
460000
|
400000
|
500000
|
500000
|
475000
|
500000
|
-
|
500000
|
|
8
|
Shear Strength @
73 F
|
psi
|
D732
|
10500
|
9000
|
10500
|
-
|
10000
|
11000
|
-
|
11000
|
|
9
|
Compressive Strength,
(% Deformation) @73 F
|
psi
|
D695
|
160000(10)
|
12000(10)
|
14000(10)
|
13000(10)
|
14000(10)
|
15000(10)
|
-
|
15000(10)
|
|
10
|
Compressive
Modulus of Elasticity @73 F
|
psi
|
D695
|
420000
|
400000
|
400000
|
425000
|
400000
|
400000
|
-
|
400000
|
|
11
|
Hardness,
Rockwell, Scale as noted @73 F
|
-
|
D785
|
M85(R115)
|
M85(R115)
|
M80(R110)
|
M80(R117)
|
M80(R115)
|
M85(R115)
|
M70
|
M85(R115)
|
|
12
|
Hardness, Durometer, Shore D @73 F
|
-
|
D2240
|
D85
|
D85
|
D85
|
-
|
D85
|
D85
|
D85
|
D85
|
|
13
|
Izod Impact, (Notched) @73 F
|
ft-lb/in of notch
|
D256 TypeA
|
0.5
|
0.4
|
0.5
|
0.9
|
0.5
|
0.4
|
-
|
0.4
|
|
14
|
Coefficient of
Friction, (Dry vs. Steel) Dynamic
|
-
|
-
|
0.20
|
0.16
|
0.20
|
0.18
|
.078
|
0.20
|
-
|
0.20
|
|
15
|
Limiting PV,
(with 4 to 1 factor of safety applied)
|
psi-ft/min
|
-
|
3000
|
10000
|
3000
|
3800
|
12300
|
3000
|
-
|
3000
|
|
THERMAL
|
16
|
Coefficient of
Linear Thermal Expansion @73 F
|
in/in/F
|
E-831 (TMA)
|
4.0E-05
|
5.5E-05
|
5.0E-05
|
5.9E-05
|
5.0E-05
|
3.5E-05
|
3.5E-05
|
3.5E-05
|
|
17
|
Heat Deflection
Temperature @ 264 psi
|
F
|
D648
|
200
|
200
|
200
|
-
|
200
|
200
|
200
|
200
|
|
18
|
Tg-Glass transition temperature,
(Amorphous)
|
F
|
D3418
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
19
|
Melting Point,
(VS=Vicat Softening Temp.)
|
F
|
D3418
|
500
|
500
|
420
|
420
|
420
|
420
|
420
|
420
|
|
20
|
Continuous
Service Temperature in Air, (Max.)
|
F
|
-
|
220
|
220
|
200
|
200
|
200
|
260
|
-
|
200
|
|
21
|
Thermal
Conductivity
|
BTU-in/hr-ft2-F
|
-
|
1.7
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
ELECTRICAL
|
22
|
Dielectric
Strength, Short Term
|
Volts/mil
|
D149
|
350
|
350
|
400
|
-
|
400
|
500
|
-
|
500
|
|
23
|
Volume Resistivity
|
ohm-cm
|
D257
|
2.5E+13
|
2.5E+13
|
2.5E+13
|
-
|
2.5E+13
|
2.5E+13
|
-
|
2.5E+13
|
|
24
|
Dielectric
Constant @ 10E6 Hz
|
-
|
D150
|
-
|
-
|
3.7
|
-
|
-
|
3.7
|
3.7
|
3.7
|
|
25
|
Dissipation
Factor @ 10E6 Hz
|
-
|
D150
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
26
|
Flammability @
3.1 mm unless noted
|
-
|
UL94
|
V-2
|
HB
|
HB
|
HB
|
HB
|
HB
|
HB
|
HB
|
|
H2O
|
27
|
Water Absorbtion, Immersion, 24 Hrs
|
% by wt.
|
D570(7)
|
0.30
|
0.30
|
0.30
|
0.22
|
0.25
|
0.30
|
0.30
|
0.30
|
|
28
|
Water Absorbtion, Saturation
|
% by wt.
|
D570(7)
|
7.00
|
7.00
|
7.00
|
7.00
|
7.00
|
7.00
|
7.00
|
7.00
|